Zhou, L.*; Zhang, H.*; Qin, T. Y.*; Hu, F. F.*; 徐 平光; Ao, N.*; Su, Y. H.; He, L. H.*; Li, X. H.*; Zhang, J. R.*; et al.
Metallurgical and Materials Transactions A, 11 Pages, 2024/00
被引用回数：0 パーセンタイル：0.02(Materials Science, Multidisciplinary)High-speed railway S38C axles undergo surface induction hardening for durability, but are susceptible to fatigue cracks from foreign object impact. The neutron diffraction method was employed to measure the residual strain in S38C axles, obtaining microscopic lattice distortion data, for the gradient layer at a depth of 8 mm under the surface. The results showed that after induction-hardening, the microscopic lattice distortion had a gradient distribution, decreasing with the distance from the surface. However, in the case of impacting speed of 600 km/m, the average microscopic lattice distortion increased with the distance from the surface, reaching a maximum augmentation of 55 pct. These findings indicate a strong experimental basis, and improve our understanding of the relationship between macroscopic residual stress and decision-making, in regard to operation and maintenance.
Ao, N.*; Zhang, H.*; Xu, H. H.*; Wu, S. C.*; Liu, D.*; 徐 平光; Su, Y. H.; Kang, Q. H.*; Kang, G. Z.*
Engineering Fracture Mechanics, 281, p.109166_1 - 109166_14, 2023/03
被引用回数：5 パーセンタイル：87.64(Mechanics)Considering the complex service environments that high-speed railway axles are subjected to, the fatigue crack growth (FCG) behavior of a structurally gradient axle steel with different pre-crack depths both in air and corrosive medium was investigated at a frequency of 5 Hz. The results indicated that in the high 
region, FCG rate was dramatically accelerated by corrosion, but the gap narrows as decreased. The accelerated corrosion FCG rate was a comprehensive result of the acceleration effect of the anodic dissolution, hydrogen-enhanced localized plasticity and the retardation effect of corrosion-induced crack-tip blunting. Despite the fact that the corrosion resistance gradually decreased as the pre-crack depth increased, the FCG rate in the corrosive medium gradually decreased. This was because fatigue loading played a more important role than corrosion in accelerating the corrosion FCG rate.